Model: GB 9948
merk: Torich
verpakkingen: verpakken in houten kisten of in zeshoekige bundels
produktiviteit: 20000 Tons per Year
vervoer: Ocean,Land,Air
Plaats van herkomst: China
Ondersteuning over: 60000 Ton per year
Certificaat: ISO9001:2008 ISO14001:2008, TS16949, CE PED, TUV, API
GS-code: 7304293000
Haven: Shanghai,Ningbo
betaling Type: L/C,T/T,D/P,Paypal,Money Gram,Western Union
Incoterm: FOB,CFR,CIF,FCA,CPT
Productnaam: GB 9948 Material10 # 20 # 12CrMo 15CrMo 12Cr1MoV Petroleum kraken Naadloze stalen buizen
Wij zijn fabrikant van naadloze stalen buizen in China, als u naadloze stalen buis, olie cilinder stalen buis, precisie naadloze stalen buis, hydraulische cilinder stalen buis wilt kopen, neem dan contact met ons op.
Uit Diameter: 3 ~ 600mm
Wanddikte: 0,5 ~ 50 mm
Toepassing: Het wordt gebruikt voor de naadloze stalen buizen voor oven, warmtewisselaars Petroleum Cracking etc.
Tabel 1 De toleranties van buitendiameter en wanddikte Eenheid: mm
Sort Code |
Manufacuring Method |
Nominal Size |
Tolerances |
||
Common Level |
High Level |
||||
W-H |
Hot Rolling (Extrusion) |
Outer Diameter D |
≤54 |
±0.50 |
±0.30 |
>54~325 |
±1%D |
±0.75%D |
|||
>325 |
±1%D |
- |
|||
Wall Thicknass S |
≤20 |
+15%S -10%S |
±10%S |
||
>20 |
+12.5%S -10%S |
±10%S |
|||
Hot Expand |
Outer Diameter D |
All |
±1%D |
||
Wall Thicknass S |
All |
±15%S |
|||
W-C |
Cold Drawn(Rolling) |
Outer Diameter D |
≤25.4 |
±0.15 |
|
>25.4~40 |
±0.20 |
||||
>40~50 |
±0.25 |
||||
>50~60 |
±0.30 |
||||
>60 |
±0.75%D |
±0.5%D |
|||
Wall Thicknass S |
≤3.0 |
±0.3 |
±0.2 |
||
>3.0 |
±10%S |
±7.5%S |
Tabel 2 De tolerantie van de minimale wanddikte-eenheid: mm
Sort Code |
Manufacturing Method |
Minimum Wall Thickness Smin |
Tolerance |
|
Common Level |
High Level |
|||
W-H |
Hot Rolling(Extrusion) |
≤4.0 |
+0.90 0 |
+0.70 0 |
>4.0 |
+25%Smin 0 |
+22%Smin 0 |
||
W-C |
Cold Drawn(Rolling) |
≤3.0 |
+0.6 0 |
+0.4 0 |
>3.0 |
+20%Smin 0 |
+15%Smin 0 |
Tabel 3 Staalkwaliteit en chemische samenstelling
Steel grade |
Chemical composition % |
|||||||||||
C |
Si |
Mn |
Cr |
Mo |
Ni |
Nb |
Ti |
V |
Cu |
P |
S |
|
≤ |
||||||||||||
10 |
0.07~ 0.13 |
0.17~ 0.37 |
0.35~ 0.65 |
≤0.15 |
≤0.15 |
≤ 0.25 |
- |
- |
≤0.08 |
≤0.20 |
0.025 |
0.015 |
20 |
0.17~ 0.23 |
0.17~ 0.37 |
0.35~ 0.65 |
≤0.25 |
≤0.15 |
≤ 0.25 |
- |
- |
≤0.08 |
≤0.20 |
0.025 |
0.015 |
12CrMo |
0.08~ 0.15 |
0.17~ 0.37 |
0.40~ 0.70 |
0.40~ 0.70 |
0.40~ 0.55 |
≤ 0.30 |
- |
- |
- |
≤0.20 |
0.025 |
0.015 |
15CrMo |
0.12~ 0.018 |
0.17~ 0.37 |
0.40~ 0.70 |
0.80~ 1.10 |
0.40~ 0.55 |
≤ 0.30 |
- |
- |
- |
≤0.20 |
0.025 |
0.015 |
12CrlMo |
0.08~ 0.15 |
0.50~ 1.00 |
0.30~ 0.60 |
1.00~ 1.50 |
0.45~ 0.65 |
≤ 0.30 |
- |
- |
- |
≤0.20 |
0.025 |
0.015 |
12CrlMoV |
0.08~ 0.15 |
0.17~ 0.37 |
0.40~ 0.70 |
0.90~ 1.20 |
0.25~ 0.35 |
≤ 0.30 |
- |
- |
0.15~ 0.30 |
≤0.20 |
0.025 |
0.015 |
12Cr2Mo |
0.08~ 0.15 |
≤0.50 |
0.40~ 0.60 |
2.00~ 2.50 |
0.90~ 1.13 |
≤ 0.30 |
- |
- |
- |
≤0.20 |
0.025 |
0.015 |
12Cr5MoI 12Cr5MoNT |
≤ 0.15 |
≤0.50 |
0.30~ 0.60 |
4.00~ 6.00 |
0.45~ 0.60 |
≤ 0.60 |
- |
- |
- |
≤0.20 |
0.025 |
0.015 |
12Cr9MoI 12Cr9MoNT |
≤ 0.15 |
0.25~ 1.00 |
0.30~ 0.60 |
8.00~ 10.00 |
0.90~ 1.10 |
≤ 0.60 |
- |
- |
- |
≤0.20 |
0.025 |
0.015 |
07Cr19Ni10 |
0.04~ 0.10 |
≤ 1.00 |
≤2.00 |
18.00~ 20.00 |
- |
8.00~ 11.00 |
- |
- |
- |
- |
0.030 |
0.015 |
07Cr18Ni11Nb |
0.04~ 0.10 |
≤ 1.00 |
≤2.00 |
17.00~ 19.00 |
- |
9.00~ 12.00 |
8C~ 1.10 |
- |
- |
- |
0.030 |
0.015 |
07Cr19Ni11NTi |
0.04~ 0.10 |
≤0.75 |
≤2.00 |
17.00~ 20.00 |
- |
9.00~ 13.00 |
- |
4C~ 0.60 |
- |
- |
0.030 |
0.015 |
022Cr17Ni12Mo2 |
≤ 0.30 |
≤1.00 |
≤2.00 |
16.00~ 18.00 |
2.00~ 3.00 |
10.00~ 14.00 |
- |
- |
- |
- |
0.030 |
0.015 |
Tabel 4 Warmtebehandelingsstandaard
Steel Grade |
Heat Treatment Standard |
10a |
Normalizing;At Temperature 880℃~940℃ |
20a |
Normalizing:At Temperature 880℃~940℃ |
12CrMob |
Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 670℃~730℃ |
15CrMob |
Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 680℃~730℃ |
12Cr1Mob |
Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 680℃~750℃ |
12Cr1MoVb |
S≤30mm:Normalizing:At Temperature 980℃~1020℃ Tempering:At Temperature 720℃~760℃ S>30mm:Quenching:At Temperature 950℃~990℃ Tempering:At Temperature 720℃~760℃ Or Normalizing:At Temperature 980℃~1020℃ (rapid cooling after Normalizing) Tempering:At Temperature 720℃~760℃ |
12Cr2Mob |
S≤30mm:Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 700℃~750℃ S>30mm:Quenching:At Temperature ≥ 900℃ Tempering:At Temperature 700℃~750℃ Or Normalizing:At Temperature 900℃~960℃ (rapid cooling after Normalizing) Tempering:At Temperature 700℃~750℃ |
12Cr5MoI |
Full Annealing or isothermal annealing |
12Cr5MoNT |
Normalizing:At Temperature 930℃~980℃ Tempering:At Temperature 730℃~770℃ |
12Cr9MoI |
Full Annealing or isothermal annealing |
12Cr9MoNT |
Normalizing:At Temperature 890℃~950℃ Tempering:At Temperature 720℃~800℃ |
07Cr19Ni10 |
Treatment with solid solving:At Temperature ≥ 1040℃ (rapid cooling after Treatment)
|
07Cr18Ni11Nb |
Treatment with solid solving: For Hot Rolled Tube At Temperature ≥ 1050℃ For Cold Drawn(rolled)Tube At Temperature ≥ 1100℃ (rapid cooling after Treatment)
|
07Cr19Ni11Ti |
Treatment with solid solving: For Hot Rolled Tube At Temperature ≥ 1050℃ For Cold Drawn(rolled)Tube At Temperature ≥ 1100℃ (rapid cooling after Treatment)
|
Tabel 5 Mechanische eigenschap
Steel Grade |
Tensile Strength Rm/MPa |
Lower yield strength Rp0.2/MPa |
Elongation A/% |
Shock absorption KV2/J |
Brinell hardness |
||
Longitudinal direction |
Transverse |
Longitudinal direction |
Transverse |
||||
≥ |
≤ |
||||||
10 |
335~475 |
205 |
25 |
23 |
40 |
27 |
- |
20 |
410~550 |
245 |
24 |
22 |
40 |
27 |
- |
12CrMo |
410~560 |
205 |
21 |
19 |
40 |
27 |
156HBW |
15CrMo |
440~640 |
295 |
21 |
19 |
40 |
27 |
170HBW |
12Cr1Mo |
415~560 |
205 |
22 |
20 |
40 |
27 |
163HBW |
12Cr2MoV |
470~640 |
255 |
21 |
19 |
40 |
27 |
179HBW |
12Cr2Mo |
450~600 |
280 |
22 |
20 |
40 |
27 |
163HBW |
12Cr5MoI |
415~590 |
205 |
22 |
20 |
40 |
27 |
163HBW |
12Cr5MoNT |
480~640 |
280 |
20 |
18 |
40 |
27 |
- |
12Cr9MoI |
460~640 |
210 |
20 |
18 |
40 |
27 |
179HBW |
12Cr9MoNT |
590~740 |
390 |
18 |
16 |
40 |
27 |
- |
07Cr19Ni10 |
≥520 |
205 |
35 |
- |
- |
187HBW |
|
07Cr18Ni11Nb |
≥520 |
205 |
35 |
- |
- |
187HBW |
|
07Cr19Ni11Ti |
≥520 |
205 |
35 |
- |
- |
187HBW |
|
022Cr17Ni12Mo2 |
≥485 |
170 |
35 |
- |
- |
187HBW |
|
If the wall thickness of the tube is less than 5mm, doesn`t have to do the hardness test |
Tabel 6 Impact energieabsorptie verzwakkingsfactor van klein monster
Specimen |
Specimen size(heightXwidth)mm |
Attenuation factor |
Standard sample |
10X10 |
1.00 |
Small sample |
10X7.5 |
0.75 |
Small sample |
10X5 |
0.50 |
Tabel 7 Diameter affakkelsnelheid van stalen buizen
Steel |
Diameter flaring rate of steel tubes/% |
||
ID/OD |
|||
≤0.6 |
>0.6~0.8 |
>0.8 |
|
Carbon structural steel |
10 |
12 |
17 |
Alloy structural steel |
8 |
10 |
15 |
Stainless(heat resistance)steel |
12 |
15 |
20 |
Tabel 8 Testitems en monsterhoeveelheid stalen buizen
Number |
Testing items |
Sampling quantity |
1 |
Chemical composition |
1 sample from each furnace |
2 |
Tensile test |
1 sample from each of two steel tubes on each batch |
3 |
Hardness test |
3 samples taken on 2 steel tubes on each batch |
4 |
Impact test |
All |
5 |
Hydraulic test |
1 sample from each of two steel tubes on each batch |
6 |
Flattening test |
2 samples taken on 2 steel tubes on each batch |
7 |
Bending test |
1 sample taken on 2 steel tubes on each furnace |
8 |
Flaring test |
2 samples taken on 2 steel tubes on each batch |
9 |
Macroscopic examination |
1 sample taken on 2 steel tubes on each furnace |
10 |
Non-metallic inclusions |
1 sample taken on 2 steel tubes on each furnace |
11 |
Eddy current testing |
All |
12 |
Magnetic flux leakage detection |
All |
13 |
Ultrasonic testing |
All |
14 |
Intergranular corrosion test |
1 sample from each of two steel tubes on each batch |
Tabel A.1 Vergelijkingstabel van vergelijkbare staalkwaliteit
No. |
GB |
Similar Steel Grade |
|||
ISO |
EN |
ASTM/ASME |
JIS |
||
1 |
10 |
- |
P195GH |
A |
STB 340 |
2 |
20 |
PH26 |
P235GH |
A-1.B |
STB 410 |
3 |
12CrMo |
- |
- |
T2/P2 |
STBA 20 |
4 |
15CrMo |
13CrMo4-5 |
13CrMo4-5 |
T12/P12 |
STBA 22 |
5 |
12Cr1Mo |
- |
10CrMo5-5 |
T11/P11 |
STBA 23 |
6 |
12Cr1MoV |
- |
- |
- |
- |
7 |
12Cr2Mo |
10CrMo9-10 |
10CrMo9-10 |
T22/P22 |
STBA 24 |
8 |
12Cr5Mo-I |
X11CrMo9-1TA |
X11CrMo5+I |
T5/P5 |
STBA 25 |
9 |
12Cr5Mo-NT |
- |
X11CrMo5+NT |
T5/P5 |
STBA 25 |
10 |
12Cr9Mo-I |
X11CrMo9-1TA |
X11CrMo9-1+I |
T9/P9 |
STBA 26 |
11 |
12Cr9Mo-NT |
- |
X11CrMo9-1+NT |
T9/P9 |
STBA 26 |
12 |
07Cr19Ni10 |
X7CrNi18-9 |
X6CrNi18-10 |
TP304H |
SUS 304H TB |
13 |
07Cr18Ni11Nb |
X7CrNiNb18-10 |
X7CrNiNb18-10 |
TP347H |
SUS 347H TB |
14 |
07Cr19Ni11Ti |
- |
X6CrNiTi18-10 |
TP321H |
SUS 321H TB |
15 |
022Cr17Ni12Mo2 |
- |
X2CrNiMo17-12-2 |
TP316L |
SUS 316L TB |
Product Categorie : Naadloze stalen buizen
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.